Fabrication and Characterization of Electrospun Nanofibrous Composite Membrane for Air Filtration

Si Cheng, Yuan-Xiang Xiao, Lian-Ying Zhao, Lv-Tao Zhu, Ren-Long Li, Guo-Cheng Zhu

DOI: 10.3993/jfbim00272

Journal of Fiber Bioengineering & Informatics, 10 (2017), pp. 223-230.

Published online: 2017-10

Preview Purchase PDF 1040 18938

Cited by

google scholar semantic scholar
Export citation
  • Abstract

One kind of composite membrane by combining electrospun nanofibrous membrane with fiberglass mesh was developed for air filtration. The fiber diameter, morphology of membranes, pressure drop and filtration efficiency of composite membrane were evaluated. The results revealed that the pressure drop and filtration efficiency of composite membrane decreased with the increase of winding speed (the higher winding speed is, the less of nanofibers are). The pressure drop of all samples at an airflow speed of 5 m/min was less than 25 Pa, which was much lower than the values from other reported work; and the highest filtration efficiency of sample in this work was more than 83% for particulate matters with 1.88 m.


  • Keywords

Electrospinning Nanofiber Light Transmittance Pressure Drop Filtration Efficiency.

  • AMS Subject Headings

  • Copyright

COPYRIGHT: © Global Science Press

  • Email address
  • BibTex
  • RIS
  • TXT
@Article{JFBI-10-223, author = {}, title = {Fabrication and Characterization of Electrospun Nanofibrous Composite Membrane for Air Filtration}, journal = {Journal of Fiber Bioengineering and Informatics}, year = {2017}, volume = {10}, number = {4}, pages = {223--230}, abstract = {

One kind of composite membrane by combining electrospun nanofibrous membrane with fiberglass mesh was developed for air filtration. The fiber diameter, morphology of membranes, pressure drop and filtration efficiency of composite membrane were evaluated. The results revealed that the pressure drop and filtration efficiency of composite membrane decreased with the increase of winding speed (the higher winding speed is, the less of nanofibers are). The pressure drop of all samples at an airflow speed of 5 m/min was less than 25 Pa, which was much lower than the values from other reported work; and the highest filtration efficiency of sample in this work was more than 83% for particulate matters with 1.88 m.


}, issn = {2617-8699}, doi = {https://doi.org/10.3993/jfbim00272}, url = {http://global-sci.org/intro/article_detail/jfbi/12572.html} }
TY - JOUR T1 - Fabrication and Characterization of Electrospun Nanofibrous Composite Membrane for Air Filtration JO - Journal of Fiber Bioengineering and Informatics VL - 4 SP - 223 EP - 230 PY - 2017 DA - 2017/10 SN - 10 DO - http://doi.org/10.3993/jfbim00272 UR - https://global-sci.org/intro/article_detail/jfbi/12572.html KW - Electrospinning KW - Nanofiber KW - Light Transmittance KW - Pressure Drop KW - Filtration Efficiency. AB -

One kind of composite membrane by combining electrospun nanofibrous membrane with fiberglass mesh was developed for air filtration. The fiber diameter, morphology of membranes, pressure drop and filtration efficiency of composite membrane were evaluated. The results revealed that the pressure drop and filtration efficiency of composite membrane decreased with the increase of winding speed (the higher winding speed is, the less of nanofibers are). The pressure drop of all samples at an airflow speed of 5 m/min was less than 25 Pa, which was much lower than the values from other reported work; and the highest filtration efficiency of sample in this work was more than 83% for particulate matters with 1.88 m.


Si Cheng, Yuan-Xiang Xiao, Lian-Ying Zhao, Lv-Tao Zhu, Ren-Long Li, Guo-Cheng Zhu. (2019). Fabrication and Characterization of Electrospun Nanofibrous Composite Membrane for Air Filtration. Journal of Fiber Bioengineering and Informatics. 10 (4). 223-230. doi:10.3993/jfbim00272
Copy to clipboard
BibteX RIS TXT
The citation has been copied to your clipboard